首页> 外文期刊>Metallurgist >Phase Composition of Light-Weight Steels and Alloys Based on the Fe-Mn-Al-C System
【24h】

Phase Composition of Light-Weight Steels and Alloys Based on the Fe-Mn-Al-C System

机译：基于Fe-Mn-Al-C体系的轻钢和合金的相组成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A Thermo-Calc program is used to calculate isothermal and polythermal sections of diagrams and phase composition for a series of alloys of the Fe-Mn-Al-Si-Mo-C-N system. Microstructure of these alloys is studied after quenching, hot and warm deformation, and ageing at 550A degrees C. It is established that the phase equilibrium diagram of the Fe-Mn-Al-C system may be used for predicting alloy structure for this system after different forms of treatment. Alloys with a single-phase gamma-region in the range 1000-1200A degrees C and containing 20% or more Mn should contain more than 1.5% C with an Al content of 7.5% and more than 2% C with a 9% aluminum content.
机译：Thermo-Calc程序用于计算Fe-Mn-Al-Si-Mo-C-N系统的一系列合金的等温线图和多相线图以及相组成。在淬火，热变形和热变形以及在550A的温度下进行时效处理之后，研究了这些合金的显微组织。已确定，Fe-Mn-Al-C体系的相平衡图可用于预测该体系的合金结构。不同的治疗方式。具有1000-1200A摄氏度范围内的单相伽马区且含有20％或更多的Mn的合金应包含1.5％以上的C（铝含量为7.5％）和2％以上的C（铝含量为9％） 。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号