首页> 外文期刊>Nanotechnology >Insitu observation of morphological change in CdTe nano-and submicron wires
【24h】

Insitu observation of morphological change in CdTe nano-and submicron wires

机译：CdTe纳米和亚微米线的形态变化的原位观察

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We report growth and characterization of CdTe wires 30-400nm in diameter by the vapor-liquid-solid technique. Individual nanowires were placed on a movable piezotube, which allowed three-dimensional motion toward a scanning tunneling microscope (STM). A bias was applied to the STM tip in contact with the nanowire, and the morphological changes due to Joule heating were observed insitu using a transmission electron microscope (TEM) in real time. For thick CdTe wires (d > ～ 150nm), the process results in the growth of superfine nanowires (SFNWs) of 2-4nm diameter on the surface of the wire. Smaller diameter nanowires, in contrast, disintegrate under the applied bias before the complete evolution of SFNWs on the surface.
机译：我们通过汽-液-固技术报告了直径为30-400nm的CdTe线的生长和表征。将各个纳米线放置在可移动的压电管上，该压电管允许向扫描隧道显微镜（STM）进行三维运动。向与纳米线接触的STM尖端施加偏压，并使用透射电子显微镜（TEM）实时观察到因焦耳热引起的形态变化。对于较厚的CdTe导线（d>〜150nm），该过程导致在导线表面上生长直径为2-4nm的超细纳米线（SFNW）。相反，直径较小的纳米线在表面上SFNW完全演化之前，在施加的偏压下会崩解。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号