首页> 外文期刊>Nanotechnology >Large-scale synthesis of single-crystalline Te nanobelts by a low-temperature chemical vapour deposition route
【24h】

Large-scale synthesis of single-crystalline Te nanobelts by a low-temperature chemical vapour deposition route

机译：低温化学气相沉积法大规模合成单晶Te纳米带

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A low-temperature chemical vapour deposition method has been successfully developed for synthesizing single-crystalline Te nanobelts in bulk quantity from Al_2Te_3 powder and H_2O. The nanobelts had a uniform single-crystal hexagonal structure with width ranging from 50 to 300 nm, thickness about 10-20 nm, and lengths up to several tens of micrometres. The growth of Te nanobelts is controlled by a vapour-solid crystal growth mechanism. The method is very simple and the as-synthesized products are pure, so it represents a practical approach to large-scale synthesis of pure single-crystal Te nanobelts.
机译：成功开发了一种低温化学气相沉积法，用于由Al_2Te_3粉末和H_2O合成大量单晶Te纳米带。纳米带具有均匀的单晶六边形结构，其宽度在50到300 nm之间，厚度在10到20 nm之间，长度可达几十微米。 Te纳米带的生长受气固晶体生长机制控制。该方法非常简单，所合成的产物是纯净的，因此它代表了大规模合成纯单晶Te纳米带的实用方法。