首页> 外文期刊>Nanotechnology >A ZnO nanowire array film with stable highly water-repellent properties
【24h】

A ZnO nanowire array film with stable highly water-repellent properties

机译：具有稳定的高疏水性的ZnO纳米线阵列膜

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Highly water-repellent surfaces have been prepared from arrayed nanowires of zinc oxide (ZnO) by a treatment with stearic acid. The layers are electrochemically deposited on a nanocrystalline seed layer from an oxygenated aqueous zinc chloride solution. An advancing contact angle ( CA) as high as 176 degrees is obtained with a very small hysteresis similar to 1 degrees. These results, supplemented by infrared spectroscopy, show that the stearic acid forms a very well-packed self-assembled monolayer. The CA measurements show a very good stability of the treated surface even when exposed to harsh conditions or long-term ambient illumination.
机译：通过用硬脂酸处理，由排列的氧化锌（ZnO）纳米线制备了高度疏水的表面。从氧化的氯化锌水溶液将这些层电化学沉积在纳米晶种层上。获得的前进接触角（CA）高达176度，而滞后很小，类似于1度。这些结果，再加上红外光谱分析，表明硬脂酸形成了一个包装得很好的自组装单分子层。即使在恶劣的条件下或长期的环境光照下，CA测量也显示出处理过的表面非常好的稳定性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号