首页> 外文期刊>Nanotechnology >Electron energy-loss spectroscopy characterization and microwave absorption of iron-filled carbon-nitrogen nanotubes
【24h】

Electron energy-loss spectroscopy characterization and microwave absorption of iron-filled carbon-nitrogen nanotubes

机译：铁填充碳氮纳米管的电子能量损失谱表征和微波吸收

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Iron-filled carbon-nitrogen (Fe/CN_x) nanotubes and iron-filled carbon (Fe/C) nanotubes were synthesized at 900 deg C through a pyrolysis reaction of ferrocene/acetonitrile and ferrocene/xylene, respectively. The differences of structure and composition between the Fe/CN_x nanotubes and Fe/C nanotubes were investigated by transmission electron microscopy and electron energy-loss spectroscopy (EELS). It was found that the morphology of Fe/CN_x nanotubes is more corrugated than that of the Fe/C nanotubes due to the incorporation of nitrogen. By comparing the Fe L_(2,3) electron energy-loss spectra of Fe/CN_x nanotubes to those of the Fe/C nanotubes, the electron states at the interface between Fe and the tubular wall of both Fe/CN_x nanotubes and Fe/C nanotubes were investigated. At the boundary between Fe and the wall of a CN_x nanotube, the additional electrons contributed from the doped 'pyridinic-like' nitrogen might transfer to the empty 3d orbital of the encapsulated iron, therefore leading to an intensity suppression of the iron L_(2,3) edge and an intensity enhancement of the carbon K edge. However, such an effect could not be found in Fe/C nanotubes. Microwave absorption properties of both Fe/CN_x and Fe/C nanocomposites at 2-18 GHz band were studied.
机译：分别通过二茂铁/乙腈和二茂铁/二甲苯的热解反应在900摄氏度下合成了铁填充碳氮（Fe / CN_x）纳米管和铁填充碳（Fe / C）纳米管。通过透射电子显微镜和电子能量损失谱（EELS）研究了Fe / CN_x纳米管和Fe / C纳米管在结构和组成上的差异。发现由于氮的引入，Fe / CN_x纳米管的形态比Fe / C纳米管的波纹更波纹。通过比较Fe / CN_x纳米管的Fe L_（2,3）电子能量损失谱与Fe / C纳米管的电子能量损失谱，电子在Fe与Fe / CN_x纳米管和Fe / CN_x纳米管的管壁之间的界面处处于电子态研究了碳纳米管。在Fe和CN_x纳米管壁之间的边界处，掺杂的类似``吡啶样''氮的贡献电子可能转移到封装铁的空3d轨道上，因此导致强度抑制L_（2 ，3）边缘和碳K边缘的强度增强。但是，在Fe / C纳米管中未发现这种效果。研究了Fe / CN_x和Fe / C纳米复合材料在2-18 GHz频段的微波吸收特性。