The preparation and mechanism studies of porous titania

机译:

获取原文
获取原文并翻译 | 示例
           

摘要

Ultrafine porous titania powders were synthesized by precipitating method with titania sulfate and ammonia as raw materials and ethanol as dispersing agent. The influences of pH and reaction temperatures on the texture of titania precursor powders were investigated. The porous titania material was formed by titania precursors calcined above 200 degrees C, and the surface area of powders changes from 541.9 m(2) g(-1) (precursor) to 762.5 m(2) g(-1) (precursors calcined at 200 degrees C). The causes of surface area reduction with calcining temperatures are grain growth and phase transformation. Micropores in porous titania samples were lost by samples calcined above 500 degrees C. On TEM photos space network of porous titania is clearly seen. (C) 2000 Published by Elsevier Science S.A. All rights reserved. References: 21

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱:kefu@zhangqiaokeyan.com

京公网安备:11010802029741号 ICP备案号:京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有
  • 客服微信

  • 服务号