首页> 外文期刊>RSC Advances >ZnS nanowall coated Ni composites: facile preparation and enhanced electromagnetic wave absorption
【24h】

ZnS nanowall coated Ni composites: facile preparation and enhanced electromagnetic wave absorption

机译：ZnS纳米壁涂覆的Ni复合材料：简便的制备方法和增强的电磁波吸收

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this work, core-shell composites with Ni cores and ZnS nanowall shells have been successfully prepared by a hydrothermal deposition method. The crystal structures, microstructures and electromagnetic (EM) properties of the samples were investigated by X-ray diffraction, scanning electron microscopy, energy disperse X-ray spectrometry, transmission electron microscopy and a network analyser (2-18 GHz). In comparison with Ni and ZnS particles, the Ni/ZnS composites show the best microwave absorption properties. The optimal reflection loss is -25.78 dB at 14.24 GHz with the thickness of 2.7 mm. The reflection loss below -10 dB (90% microwave absorption) is 4.72 GHz (11.52-16.24 GHz) with only a thickness of 2.7 mm. The enhanced microwave absorption capabilities of Ni/ZnS composites were due to good electromagnetic impedance matching, interfacial relaxation and unique wall-like ZnS shells.
机译：在这项工作中，通过水热沉积法成功地制备了具有Ni核和ZnS纳米壁壳的核-壳复合材料。通过X射线衍射，扫描电子显微镜，能量分散X射线光谱，透射电子显微镜和网络分析仪（2-18 GHz）研究了样品的晶体结构，微结构和电磁（EM）特性。与Ni和ZnS颗粒相比，Ni / ZnS复合材料显示出最佳的微波吸收性能。最佳反射损耗在14.24 GHz时为-25.78 dB，厚度为2.7 mm。低于-10 dB（90％的微波吸收）的反射损耗为4​​.72 GHz（11.52-16.24 GHz），厚度仅为2.7 mm。 Ni / ZnS复合材料的增强的微波吸收能力归因于良好的电磁阻抗匹配，界面弛豫和独特的壁状ZnS壳层。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号