首页> 外文期刊>Optics Letters >Carrier-mediated 1.55 (mu)m photoluminescence from single Er~(3+) center in SnO_(2) nanocrystals
【24h】

Carrier-mediated 1.55 (mu)m photoluminescence from single Er~(3+) center in SnO_(2) nanocrystals

机译：SnO_（2）纳米晶体中单个Er〜（3+）中心的载流子介导的1.55μm光致发光

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We report the successful incorporation of Er~(3+) ions into SnO_(2) nanocrystals via a solvothermal method, with a resulting Er~(3+) concentration of the order of 10~(19) cm~(-3). Upon excitation above the SnO_(2) bandgap at 300 nm, intense and well-resolved Er~(3+)-related photoluminescence (PL) at 1.55 (mu)m was observed at room temperature. The results of PL excitation and ultraviolet/visible diffuse reflectance spectra indicate that the excitation is a carrier-mediated process with an energy transfer from the SnO_(2) host to Er~(3+). For the above-gap excitation, only a single type of Er~(3+) luminescence center located at a centrosymmetric site was identified. The near-infrared luminescence dynamics and the weak PL thermal quenching of Er~(3+) were also revealed.
机译：我们报道了通过溶剂热法成功地将Er〜（3+）离子掺入SnO_（2）纳米晶体中，导致Er〜（3+）浓度约为10〜（19）cm〜（-3）。在300nm处在SnO_（2）带隙以上激发后，在室温下观察到1.55μm的强烈且良好分辨的Er〜（3+）相关的​​光致发光（PL）。 PL激发和紫外/可见漫反射光谱的结果表明，该激发是载流子介导的过程，其能量从SnO_（2）主体转移到Er〜（3+）。对于上述间隙激发，仅鉴定出位于中心对称位点的单一类型的Er〜（3+）发光中心。还揭示了Er〜（3+）的近红外发光动力学和弱PL热猝灭。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号