首页> 外文期刊>Optics Letters >Photorefractive recording in LiNbO_(3):Mn
【24h】

Photorefractive recording in LiNbO_(3):Mn

机译：LiNbO_（3）：Mn中的光折变记录

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The dynamic range, sensitivity, and dark decay of holographic recording of wavelength 458 nm in LiNbO_(3) crystals doped with 0.2-at.% Mn with different oxidation states have been measured. The measured sensitivity is 0.5 cm/J and is found to be independent of the oxidation state, and the largest M/# obtained is 12/mm (extraordinary light polarization; light wavelength, 458 nm). This combination of very large M/# and high sensitivity is in strong contrast with results for LiNbO_(3):Fe for which a direct trade-off exists between M/# and sensitivity. The activation energy of the dark decay of holograms stored in these LiNbO_(3):Mn crystals is ～1.0 eV, which is characteristic of proton compensation and leads to a projected lifetime of holograms of three years at room temperature.
机译：在掺杂了0.2at。％Mn和不同氧化态的LiNbO_（3）晶体中，测量了波长458 nm全息记录的动态范围，灵敏度和暗衰减。测得的灵敏度为0.5 cm / J，并且与氧化态无关，并且获得的最大M /＃为12 / mm（非常规光偏振;光波长458 nm）。 M /＃非常大且灵敏度高的这种组合与LiNbO_（3）：Fe的结果形成强烈对比，LiNbO_（3）：Fe的结果在M /＃和灵敏度之间存在直接权衡。这些LiNbO_（3）：Mn晶体中存储的全息图的暗衰变的活化能为〜1.0 eV，这是质子补偿的特征，导致全息图在室温下的预期寿命为三年。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号