首页> 外文期刊>Russian journal of electrochemistry >Electrochemical properties of composition solid electrolytes LiClO4-MgO
【24h】

Electrochemical properties of composition solid electrolytes LiClO4-MgO

机译：组成固体电解质LiClO4-MgO的电化学性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Composition solid electrolytes (1 - x)LiClO4-xMgO are synthesized and their physicochemical properties are studied. According to the data of differential scanning calorimetry, for sufficiently high oxide concentrations, all lithium perchlorate is present in the composite in the amorphous state. Impedance spectroscopic studies demonstrate that the conductivity of composites passes through a maximum at x = 0.8-0.9, reaching similar to 10(-2) S/cm at 200A degrees C. Based on voltammetric characteristics, it is shown that the voltage of electrochemical decomposition of composites in vacuum does not exceed 3.5-4.0 V, decreasing to 1.8-2.0 V in humid atmosphere. The conductivity of studied composites in vacuum may apparently be attributed to lithium ions, and these solid electrolytes can be used in solid-state electrochemical lithium cells.
机译：合成了固体电解质（1-x）LiClO4-xMgO，并对其理化性质进行了研究。根据差示扫描量热法的数据，对于足够高的氧化物浓度，所有高氯酸锂以非晶态存在于复合物中。阻抗谱研究表明，复合材料的电导率在x = 0.8-0.9时通过最大值，在200A时达到10（-2）S / cm。基于伏安特性，表明电化学分解的电压真空中的复合材料最大不超过3.5-4.0 V，在潮湿的环境中降至1.8-2.0V。研究的复合材料在真空中的电导率显然可以归因于锂离子，并且这些固体电解质可用于固态电化学锂电池。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号