首页> 外文期刊>Scripta materialia >A high-strength Mg-Ni-Y alloy sheet with a long-period ordered phase prepared by hot-rolling
【24h】

A high-strength Mg-Ni-Y alloy sheet with a long-period ordered phase prepared by hot-rolling

机译：通过热轧制备具有长周期有序相的高强度Mg-Ni-Y合金薄板

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Ternary Mg_(90.5)Ni_(3.25)Y_(6.25) (at percent) cast alloy consisting of a long-period ordered (LPO) phase and alpha-Mg was rolled to 70 percent thickness reduction at 623K. After annealing at 673K for 6 h, kink bands of the LPO phase and a-Mg grains of about 700 nm were observed in the Mg_(90.5)Ni_(3.25)Y_(6.25) alloy sheet. The alloy sheet exhibited a yield stress, an ultimate tensile strength and an elongation of 460 MPa, 526 MPa and 8 percent, respectively, at room temperature, and 301 MPa, 345 MPa and 12 percent, respectively, at 523K.
机译：将由长周期有序（LPO）相和α-Mg组成的三元Mg_（90.5）Ni_（3.25）Y_（6.25）（at％）铸造合金在623K轧制至厚度减少70％。在673K退火6小时后，在Mg_（90.5）Ni_（3.25）Y_（6.25）合金薄板中观察到LPO相的扭折带和约700 nm的a-Mg晶粒。该合金板在室温下的屈服应力，极限拉伸强度和伸长率分别为460 MPa，526 MPa和8％，在523K下分别为301 MPa，345 MPa和12％。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号