首页> 外文期刊>Scripta materialia >Joining of ZrB_2-based ultra-high-temperature ceramic composites using Pd-based braze alloys
【24h】

Joining of ZrB_2-based ultra-high-temperature ceramic composites using Pd-based braze alloys

机译：钯基钎料与ZrB_2基超高温陶瓷复合材料的连接

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Hot-pressed ZrB_2-SiC and composites with carbon (ZSC) or SCS-9a SiC fibers (ZSS) were joined using Pd-base brazes, Palco (65 percent Pd-35 percent Co) and Palni (60 percent Pd-40 percent Ni). Joint integrity was exhibited by the defect-free ZS/Palco/ZS joints with large interaction zones. The ZSS/Palco and ZSC/Palco joints revealed substantial chemical interaction and interfacial cracking due to residual stresses. The joints with Palni exhibited either poor wetting/bonding or cracking. The ZS/Palco joints displayed high Knoop hardness within the ZS region and lower hardness within the Palco interlayer.
机译：使用Pd基钎料，Palco（65％Pd-35％Co）和Palni（60％Pd-40％Ni）将热压ZrB_2-SiC以及含碳的复合材料（ZSC）或SCS-9a SiC纤维（ZSS）连接在一起）。具有大相互作用区域的无缺陷ZS / Palco / ZS接头具有良好的接头完整性。 ZSS / Palco和ZSC / Palco接头由于残余应力而显示出大量的化学相互作用和界面开裂。帕尔尼接头的润湿性/粘结性或开裂性均较差。 ZS / Palco接头在ZS区域显示出较高的努氏硬度，而在Palco夹层内部显示出较低的硬度。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号