首页> 外文期刊>Scripta materialia >Effect of Gd_2O_3 on the thermal conductivity of ZrO_2-4 mol.% Y_2O_3 ceramics fabricated by spark plasma sintering
【24h】

Effect of Gd_2O_3 on the thermal conductivity of ZrO_2-4 mol.% Y_2O_3 ceramics fabricated by spark plasma sintering

机译：Gd_2O_3对火花等离子体烧结制备的ZrO_2-4 mol％Y_2O_3陶瓷导热系数的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Porous and dense ZrO_2-4 mol.% Y_2O_3 ceramics were fabricated by spark plasma sintering at 1100 and 1500 °C. The porosity of the ceramics sintered at 1100 °C increased with the addition of ～0-5 mol.% Gd_2O_3. In contrast, the ceramics sintered at 1500 °C showed full density regardless of the amount of Gd_2O_3 addition. The fluorite-type Gd_2Zr_2O_7 phase was formed as the second phase in the tetragonal ZrO_2 matrix. The thermal diffusivity and thermal conductivity of sintered ZrO_2-4 mol.% Y_2O_3 decreased with increasing Gd_2O_3 addition.
机译：通过在1100和1500°C下进行火花等离子体烧结，制备了多孔致密的ZrO_2-4 mol。％Y_2O_3陶瓷。随着〜0-5 mol。％Gd_2O_3的加入，在1100°C烧结的陶瓷的孔隙率增加。相反，在1500℃下烧结的陶瓷显示出全密度，而与Gd_2O_3的添加量无关。在四方ZrO_2基体中形成了萤石型Gd_2Zr_2O_7相作为第二相。随着Gd_2O_3添加量的增加，ZrO_2-4 mol％Y_2O_3的热扩散系数和导热系数降低。