首页> 外文期刊>Scripta materialia >Grain size distribution in 3 mol.% yttria-stabilized zirconia sintered with a small AC electric field
【24h】

Grain size distribution in 3 mol.% yttria-stabilized zirconia sintered with a small AC electric field

机译：在3摩尔％氧化钇稳定的氧化锆中用小交流电场烧结后的晶粒尺寸分布

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The grain size stereology in 3 mol.% yttria-stabilized zirconia sintered with a small AC field was essentially the same as in specimens sintered without field or with an equivalent DC field. With the DC field there was no clear difference adjacent to the positive electrode compared to near the negative electrode. Thus, neither polarization nor stereology are major factors in the greater retard^ ing effect of an AC field on grain growth compared to an equivalent DC field.
机译：在3摩尔％的氧化钇稳定的氧化锆中，用较小的交流电场进行烧结，其晶粒尺寸立体与在无电场或等效的直流电场中进行烧结的试样基本相同。在直流电场下，与靠近负极相比，靠近正极没有明显的差异。因此，与等效的直流场相比，极化和立体学都不是交流场对晶粒生长更大的延迟效应的主要因素。