首页> 外文期刊>Separation and Purification Technology >Preparation of inner-side tubular zeolite NaA membranes in a continuous flow system
【24h】

Preparation of inner-side tubular zeolite NaA membranes in a continuous flow system

机译：连续流动系统中内侧管状NaA沸石膜的制备

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Zeolite NaA membranes were synthesized on the inner side of porous titania(rutile)asymmetric tubular supports in a flow system where the synthesis gel was circulated through the support with flow rates in the range 1.5-4 mL min~(-1)by the action of gravity.The syntheses were carried out hydrothermally at 358 K for 6-7h either with or without previous brush-seeding of the supports.The membranes(10-20 mu m in thickness)showed great ability to dehydrate ethanol/water mixtures(92:8,w/w)by pervaporation with selectivities and fluxes,respectively,up to 8500 and 1.2 kg m~(-2)h~(-1)at 323 K.The role of intercrystalline defects in the pervaporation performance of the synthesized membranes was also investigated.
机译：在流动系统中在多孔二氧化钛（金红石）不对称管状支撑物的内侧合成沸石NaA膜，其中合成凝胶通过该作用在流速为1.5-4 mL min〜（-1）的范围内循环通过支撑物合成过程在358 K水热下进行6-7h（有或没有预先刷涂载体）。膜（厚度为10-20μm）显示出强大的脱水乙醇/水混合物的能力（92选择性和通量的全蒸发分别在8500和1.2 kg m〜（-2）h〜（-1）的条件下达到8：w / w）。晶间缺陷在合成材料的全蒸发性能中的作用膜也进行了研究。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号