首页> 外文期刊>Smart Materials & Structures >Magnetoelectric coupling and the hydrogen effect on Ni-PZT-Ni trilayers made by electrodeposition
【24h】

Magnetoelectric coupling and the hydrogen effect on Ni-PZT-Ni trilayers made by electrodeposition

机译：电沉积Ni-PZT-Ni三层的磁电耦合和氢效应

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The magnetoclectric (ME) coupling from 20 Hz to 100 kHz and the hydrogen effect on Ni-PZT-Ni trilayer composites made by electrodeposition have been investigated. The results show that the magnetoelectric voltage coefficient, alpha(E), 31, increases with increased Ni layer thickness, up to alpha(E), 31 = 1.6 V cm(-1) Oe(-1). The ME voltage coefficient decreases with the increase of hydrogen concentration. To prevent the degradation of ME coupling, the plating solution and process parameters of electrodeposition should be chosen suitably. Moreover, an additional outgassing process after electrodeposition can reduce the hydrogen concentration and effectively promote ME coupling.
机译：研究了从20 Hz到100 kHz的磁电耦合（ME）以及氢对电沉积Ni-PZT-Ni三层复合材料的影响。结果表明，磁电电压系数α（E）31随着Ni层厚度的增加而增加，直至α（E）31 = 1.6 V cm（-1）Oe（-1）。 ME电压系数随着氢浓度的增加而降低。为了防止ME耦合性能下降，应适当选择电镀液和电镀工艺参数。而且，电沉积后的附加除气过程可以降低氢浓度并有效地促进ME耦合。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号