首页> 外文期刊>Philosophical Magazine Letters >Thermomagnetic gravimetry study of crystallization behaviour in amorphous Fe-Si-B-Nb alloys
【24h】

Thermomagnetic gravimetry study of crystallization behaviour in amorphous Fe-Si-B-Nb alloys

机译：热磁重量法研究非晶态Fe-Si-B-Nb合金的结晶行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effect of the Nb content on the crystallization process of amorphous Fe_(84-x)Si_6B_(10)Nb_x alloys has been investigated using thermomagnetic gravimetry (TMG). In the TMG measurement, the sample weight was electronically zero-balanced, and then an apparent weight (AW) applied by placing a magnet beneath the sample pan. The heating treatment was carried out over temperature range between 373 and 1093 K, in order to detect the formation of a ferromagnetic crystallization-induced phase. The form of the TMG curve changed markedly in the vicinity of 2-3 at.% Nb. In the alloys containing less than 2 at.% Nb, a two-stage increase in AW was observed with increasing temperature, but only a single-stage increase occurred for the alloys containing more than 3 at.% Nb. On the basis of these results, it is inferred that the Nb content plays a key role in the structure of the amorphous phase, supporting our recent claim for a mechanism of nanocrystallization.
机译：使用热磁重量分析法（TMG）研究了Nb含量对非晶Fe_（84-x）Si_6B_（10）Nb_x合金结晶过程的影响。在TMG测量中，对样品重量进行电子零平衡，然后通过将磁体放在样品盘下方来施加表观重量（AW）。为了检测铁磁结晶诱导相的形成，在373〜1093K的温度范围内进行了加热处理。 TMG曲线的形式在2-3at。％Nb附近显着变化。在含有少于2 at。％Nb的合金中，随着温度的升高，观察到AW呈两阶段增加，但是对于含有超过3 at。％的Nb的合金，只有单阶段增加。根据这些结果，可以推断出Nb含量在非晶相的结构中起着关键作用，这支持了我们最近对纳米晶化机理的主张。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号