Burner Rig Test of Economizer and Superheater Boiler Tube Alloys

机译：省煤器和过热器锅炉管合金的燃烧器试验

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Economizer and superheater boiler tube alloys of 1018 carbon steel, 2-1/4Cr 1Mo steel, and 316, 321, and 347 stainless steels were exposed to burner rig tests at 310 deg F and 975 deg F (155 deg C and 524 deg C), which respectively are typical economizer and superheater temperatures. The tests were made using MIL-F-16884H Navy distillate fuel with 0.0 and 0.3 ppm vanadium content. This was done to reveal problems that might result from adding vanadium to the fuel. The corrosion of the alloys at 975 F (155 C) did not significantly increase in the 0.3 ppm vanadium test. However, it did appreciably increase at 310 F (155 C). This increase was related to sulfuric acid condensation. The dewpoint of the sulfuric acid may have been raised by the presence of vanadium. The 316 stainless had the best resistance to this corrosion. Boiler tubes, Stainless steel, Burner rig, High temperature corrosion. (JES)

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号