首页> 美国政府科技报告 >Mechanisms of Hydrogen Embrittlement - Crack Growth in a Low-Alloy Ultra-High-Strength Steel Under Cyclic and Sustained Stresses in Gaseous Hydrogen.
【24h】

Mechanisms of Hydrogen Embrittlement - Crack Growth in a Low-Alloy Ultra-High-Strength Steel Under Cyclic and Sustained Stresses in Gaseous Hydrogen.

机译：氢脆的机理 - 低合金超高强度钢在气态氢循环和持续应力下的裂纹扩展。

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Rates of crack growth in a low-alloy ultra-high-strength steel (D6aC) under cyclic and sustained stresses have been measured as functions of stress-intensity, for different cyclic wave-forms and frequencies, in low pressure (13.3 kPa) hydrogen, dry air, and vacuum (.001 Pa) environments; sustained-load cracking in liquid mercury was also studied. Frequency and wave-form had large effects on rates of fatigue-crack growth in hydrogen but little influence on fatigue in air and vacuum. For triangular wave-forms, rates of crack growth in hydrogen were determined mainly by the stress-intensity range and the load-rise time. For square-wave loading, rates of crack growth in hydrogen were proportional to the time at maximum load. Quantitative relationships between rates of cracking under sustained and cyclic loads were not found. Many similarities between hydrogen-embrittlement and liquid-metal embrittlement (e.g. surfaces of the intercrystalline fractures induced by hydrogen and mercury were sometimes indistinguishable) suggested that the mechanism of embrittlement is basically the same in both cases. It is considered that previous explanations for embrittlement are not consistent with the present fractographic observations (e.g. dimpled transcrystalline fractures were sometimes observed after crack growth in mercury and hydrogen). The present results suggest that the effects of hydrogen and liquid-metal environments on crack growth can generally be explained on the basis that chemisorption influences interatomic bonds/spacings at surfaces (crack tips) and thereby facilitates nucleation of dislocations at crack tips.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号