首页> 美国政府科技报告 >Microstructure, Composition and Crystallography of Aalbrog Lion Brand DanishWhite Cement
【24h】

Microstructure, Composition and Crystallography of Aalbrog Lion Brand DanishWhite Cement

机译：aalbrog Lion牌丹麦白水泥的微观结构，成分和晶体学

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The morphology and crystallography of fully hardened Aalbrog Lion Brand DanishWhite cement paste (water cement ratio 0.25) were examined using x-ray diffraction, optical and scanning electron microscopy with energy dispersive x-ray analysis (EDX) and transmission electron microscopy and EDX. These experiments showed the hardened cement to be mostly comprised of equiaxed particles of 3CaO.SiO2 with diameter of the order of 10 microns and larger often surrounded by inner and outer regions of an amorphous gel-like matrix with an average composition of about 1.75CaO.SiO2.3H2O (C-S-H) in which the CaO/SiO2 ratio varied from about 0.3 to 5.74. The hydrated regions were also found to contain significant amounts of Ca(OH)2. Small amounts of ettringite (Ca6Al2(SO4,SiO4,CO3)3 (OH)12.26H2O) were also detected. In addition, selected area electron diffraction of the C-S-H matrix revealed diffuse rings, indicating the presence of short range ordering. The morphology of C-S-H matrix was found to be comprised of small 'cells' of size approximately 5 nm which are no doubt responsible for the good mechanical properties of this particular hardened cement paste. These results were also found to be in excellent agreement with previous research on this topic.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号