首页> 美国政府科技报告 >Long-Term Corrosion Behavior of Alloy 22 in 5 M CaCl2 at 120 C
【24h】

Long-Term Corrosion Behavior of Alloy 22 in 5 M CaCl2 at 120 C

机译：合金22在5℃CaCl2中在120℃下的长期腐蚀行为

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In conditions where tight crevices exist in hot chloride containing solutions Alloy 22 may suffer crevice corrosion. The occurrence (or not) of crevice corrosion in a given environment (e.g. salt concentration and temperature), is governed by the values of the critical potential (E(sub crit)) for crevice corrosion and the corrosion potential (E(sub corr)). This paper discusses the evolution of E(sub corr) and corrosion rate (CR) of creviced Alloy 22 specimens in 5 M calcium chloride (CaCl(sub 2)) at 120 C. Tested specimens included non-creviced rods and multiple creviced assemblies (MCA) both non-welded (wrought) and welded. Results show that Alloy 22 suffers crevice corrosion under the open circuit conditions in the aerated hot CaCl(sub 2) brine. However, after more than a year immersion the propagation of crevice corrosion was not significant. The general corrosion rate decreased or remained unchanged as the immersion time increased. For rods and MCA specimens, the corrosion rate was lower than 100 nm/year after more than a year immersion time.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号