首页> 美国政府科技报告 >Polycrystalline Thin-Film Cadmium Telluride Solar Cells Fabricated by Electrodeposition;
【24h】

Polycrystalline Thin-Film Cadmium Telluride Solar Cells Fabricated by Electrodeposition;

机译：电沉积法制备多晶薄膜碲化镉太阳电池;

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This report summarizes work performed by the Colorado School of Mines Department of Physics under this subcontract. Based on the studies conducted, researchers increased the efficiency of the cells with electrodeposited CdTe and CBD CdS by 3 on average (30 relative %). The improvement came from 1. Optimization of CdS initial thickness taking into account CdS consumption of CdTe during the CdTe/CdS post-deposition treatment; optimization of CdS post- deposition treatment with CdCl2 aimed at prevention of Te diffusion intoCdS and improvement of the CdS film morphology and electronic properties. That led to a considerable increase in short circuit current, by 13% on average. 2. Optimization of CdTe thickness and post-deposition treatment which led to a significant increase in Voc, by ;70 mV. The highest Voc obtained exceeded 800 mV. 3. Development of a ZnTe:Cu/Metal back contact processing procedure that included selection of optimal Cu content, deposition regime and post-deposition treatment conditions. As a result, back contact resistance as low as 0.1W-cm2 was obtained. The cell stability was measured on exposure to accelerated stress conditions. Preliminary studies of some new approaches to improvement of CdS/ CdTe structure were conducted.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号