Non-destructive ion beam analysis techniques have been employed to examine the radiation damage in MgAl(sub 2)O(sub 4) spinel single crystals irradiated with fast neutrons at 400 and 750(degrees)C to high fluences ((>=)5 x 10(sup 22) n/cm(sup 2), E(sub n) > 0.1 MeV). Rutherford backscattering and ion channeling measurements using 1-4 MeV He ion beams revealed that the radiation damage saturated after irradiation at 400(degrees)C to 50 displacements per atom. The energy dependence of dechanneling indicated the dominant extended defects present in the highly irradiated spinel are in the form of dislocations. Channeling angular scans of particle induced x-ray emission further suggested that neutron irradiation tends to randomize cation distribution for Mg(sup 2+) and Al(sup 3+) cations on the lattice sites. These results are compared to the microstructure observations of Kinoshita, et al. and the neutron scattering results of Sickafus, et al.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号