首页> 美国政府科技报告 >Influence of stacking faults and alloy composition on irradiation induced amorphization of ZrCr(sub 2), ZrFe(sub 2) and Zr(sub 3)(Fe(sub 1-x),Ni(sub x))
【24h】

Influence of stacking faults and alloy composition on irradiation induced amorphization of ZrCr(sub 2), ZrFe(sub 2) and Zr(sub 3)(Fe(sub 1-x),Ni(sub x))

机译：堆垛层错和合金成分对ZrCr（sub 2），ZrFe（sub 2）和Zr（sub 3）（Fe（sub 1-x），Ni（sub x））辐照诱导非晶化的影响

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

These Zr-based intermetallics were irradiated with high-energy electrons at the ANL HVEM/Tandem facility. Although ZrCr(sub 2) and ZrFe(sub 2) have the same Laves phase C15 fcc crystal structure, their critical temperatures for amorphization under electron irradiation were 180 and 80 K, showing that Cr substitution for Fe in the sublattice had a marked effect on annealing. The low temperature dose to amorphization was higher in ZrFe(sub 2) than in ZrCr(sub 2) by a factor of two. Presence of a high density of stacking faults had a strong effect on amorphization in both compounds causing the critical temperature to be increased by 10-15 K. By contrast, addition of Ni to Zr(sub 3)(Fe(sub 1-x),Ni(sub x)) had no effect on amorphization behavior for x=0.1 and 0.5. These results are discussed in terms of current models of amorphization based on defect accumulation and attainment of a critical damage level, such as given by the Lindemann criterion.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号