CONTINUOUS CASTING METHOD OF Cu-Zn-Si-BASED ALLOY, AND Cu-Zn-Si-BASED ALLOY MATERIAL
CONTINUOUS CASTING METHOD OF Cu-Zn-Si-BASED ALLOY, AND Cu-Zn-Si-BASED ALLOY MATERIAL
展开▼
机译:Cu-Zn-Si基合金和Cu-Zn-Si基合金的连续铸造方法
展开▼
页面导航
摘要
著录项
相似文献
摘要
PROBLEM TO BE SOLVED: To provide a continuous casting method of a Cu-Zn-Si-based alloy, that allows an oscillation mark depth to be sufficiently reduced and, allows an ingot of superior surface quality to be produced as a result.;SOLUTION: The continuous casting method of Cu-Zn-Si-based alloy is provided, in which continuous casting is carried out by intermittently drawing out a rod-like or a tubular ingot consisting of Cu-Zn-Si-based alloy which has a Cu content of 69 mass% to 79 mass%, an Si content of 2.0 mass% or more and less than 4.0 mass%, and a cross-sectional area of 10,000 mm2 or less. In the continuous casting method of the Cu-Zn-Si-based alloy, an intermittent withdrawal cycle consists of: a withdrawal operation in which a maximum movement speed used in moving the ingot in a withdrawal direction is Dmax, and a movement speed toward the withdrawal direction is 0.1×Dmax or higher; and a stopping operation in which the movement speed toward the withdrawal direction is less than 0.1×Dmax. In the intermittent withdrawal cycle, a movement distance of the ingot in the withdrawal direction is 5 mm or more, and stopping operation time TS in one intermittent withdrawal cycle is three seconds or longer.;COPYRIGHT: (C)2014,JPO&INPIT
展开▼
机译:解决的问题:提供一种Cu-Zn-Si基合金的连续铸造方法,该方法可以充分减小振荡痕迹的深度,从而可以生产出具有优良表面质量的铸锭。 :提供一种Cu-Zn-Si基合金的连续铸造方法,其中,通过间歇地抽出由具有Cu的Cu-Zn-Si基合金组成的棒状或管状铸锭来进行连续铸造。 Si含量为69〜79质量%,Si含量为2.0质量%以上且小于4.0质量%,截面积为10,000mm 2 Sup>以下。在Cu-Zn-Si基合金的连续铸造方法中,间歇的退出循环包括:退出操作,其中在沿退出方向移动铸锭时使用的最大移动速度为D max Sub。 >,并且向撤回方向的移动速度为0.1×D max Sub>或更高;停止动作,朝向退避方向的移动速度小于0.1×D max Sub>。在间歇退出循环中,铸锭在退出方向上的移动距离为5 mm或更大,并且在一个间歇退出周期中的停止操作时间T S Sub>为三秒或更长。 C)2014,日本特许厅&INPIT
展开▼