首页> 外国专利> Electrodes for welding and how to create wear-resistant layer on the surface of the metallurgical equipment Surfacing using electrodes

Electrodes for welding and how to create wear-resistant layer on the surface of the metallurgical equipment Surfacing using electrodes

机译：焊接用焊条以及如何在冶金设备的表面上形成耐磨层使用焊条进行堆焊

页面导航
  • 摘要
  • 著录项
  • 相似文献

摘要

FIELD: process engineering.;SUBSTANCE: invention may be used for surfacing parts subjected to active intensive wear effects at higher temperatures and multiple temperature differences, for example, hot rolling rolls, etc. electrode outer surface is made of steel or nonferrous metal. Powder filler comprises components in the following ratio, in wt %: tungsten carbide, at least - 50, cobalt - 6-10, nickel - 3-4, titanium carbide - 5-7, copper - 0.25-0.5, iron powder - 10-20, fluorite - 5-10, rutile concentrate - 4-7. To make antiwear layer on foundry equipment surface is performed by depositing aforesaid composition by electrode at the rate of 100-150 m/h at current density of 200-450 A/mm to antiwear layer thickness of 1-12 mm.;EFFECT: longer life at operation at 750 to 1150°C.;5 cl, 1 tbl, 7 ex
机译：领域：本发明可用于在高温和多个温差下经受主动强烈磨损影响的零件的表面处理，例如热轧辊等。电极外表面由钢或有色金属制成。粉末填料包括以下重量百分比的组分：碳化钨，至少-50，钴-6-10，镍-3-4，碳化钛-5-7，铜-0.25-0.5，铁粉-10 -20，萤石-5-10，金红石精矿-4-7。在铸造设备表面制备抗磨层的方法是，通过以100-150 m / h的速度在200-450 A / mm的电流密度下以100-150 m / h的速度沉积上述组合物，以形成1-12 mm的抗磨层;效果：更长寿命在750至1150°C下运行; 5 cl，1 tbl，7 ex

著录项

相似文献

  • 专利
  • 外文文献
  • 中文文献
获取专利

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号