首页> 外国专利> Nickel-chromium-cobalt-molybdenum-alloy, useful e.g. in tubes, comprises e.g. chromium, iron, carbon, manganese, silicon, cobalt, copper, molybdenum, titanium, aluminum, phosphorus, sulfur, boron, niobium, nitrogen, magnesium and calcium

Nickel-chromium-cobalt-molybdenum-alloy, useful e.g. in tubes, comprises e.g. chromium, iron, carbon, manganese, silicon, cobalt, copper, molybdenum, titanium, aluminum, phosphorus, sulfur, boron, niobium, nitrogen, magnesium and calcium

机译：镍-铬-钴-钼合金，例如在管中，包括例如铬，铁，碳，锰，硅，钴，铜，钼，钛，铝，磷，硫，硼，铌，氮，镁和钙

页面导航

摘要
著录项
相似文献

摘要

Nickel-chromium-cobalt-molybdenum-alloy (I) comprises chromium (20-24 wt.%), iron (= 1.5 wt.%), carbon (0.03-0.1 wt.%), manganese (= 0.5 wt.%), silicon (= 0.25 wt.%), cobalt (10-15 wt.%), copper (= 0.1 wt.%), molybdenum (9-10.5 wt.%), titanium (0.1-0.8 wt.%), aluminum (0.3-2 wt.%), phosphorus (less than 0.012 wt.%), sulfur (less than 0.005 wt.%), boron (greater than 0.02 to less than 0.08 wt.%), niobium (0.2-2 wt.%), nitrogen (= 0.015 wt.%), magnesium (= 0.006 wt.%), calcium (= 0.01 wt.%), vanadium (= 0.05 wt.%), nickel (balance amount) and incidental impurities.

机译：镍铬钴钼合金（I）包括铬（20-24 wt。％），铁（= 1.5 wt。％），碳（0.03-0.1 wt。％），锰（= 0.5 wt。％），硅（= 0.25 wt。％），钴（10-15 wt。％），铜（= 0.1 wt。％），钼（9-10.5 wt。％），钛（0.1-0.8 wt。％），铝（0.3-2重量％），磷（小于0.012重量％），硫（小于0.005重量％），硼（大于0.02至小于0.08重量％），铌（0.2-2重量％）。％（重量），氮（＝ 0.015重量％），镁（＝ 0.006重量％），钙（＝ 0.01重量％），钒（＝ 0.05重量％），镍（余量）和附带杂质。

著录项

公开/公告号DE102010011609A1

专利类型
公开/公告日2011-09-22

原文格式PDF
申请/专利权人 THYSSENKRUPP VDM GMBH;
展开▼

申请/专利号DE20101011609
发明设计人 KLOEWER JUTTA;RALF-UDO HUSEMANN;TEWES JUERGEN;
展开▼

申请日2010-03-16
分类号C22C19/03;
国家 DE
入库时间 2022-08-21 17:47:20

相似文献

专利
外文文献
中文文献