METHOD FOR MANUFACTURING COLORED FILM-COATED GLASS ARTICLE AND COLORED FILM-COATED GLASS ARTICLE

机译：彩膜玻璃制品和彩膜玻璃制品的制造方法

页面导航

摘要
著录项
相似文献

摘要

PROBLEM TO BE SOLVED: To provide a method for manufacturing a colored film-coated glass article which is yellow to orange and enhanced in chroma and having a desired transmitted light color tone even in the case of heat-treating at ≥400°C. ;SOLUTION: A colored film forming solution containing, by weight, 45-93% silicon oxide material (expressed in terms of SiO2), 3-30% titanium oxide material (expressed in terms of TiO2), for which at least 80% of the titanium oxide material (expressed in terms of TiO2) is a titanium oxide material chelated by β-diketone, and 5-25% fine silver particle material (expressed in terms of Ag) as the main components is applied to the surface of a glass substrate, and the formed film is irradiated with UV and then heated to manufacture a colored film-coated glass article.;COPYRIGHT: (C)2001,JPO

机译：解决的问题：提供一种制造涂有色膜的玻璃制品的方法，该制品为黄色至橙色并且色度增强并且即使在400℃下进行热处理也具有所需的透射光色调。 ;解决方案：一种彩色成膜溶液，按重量计包含45-93％的氧化硅材料（以SiO2表示），3-30％的氧化钛材料（以TiO2表示），其中至少80％氧化钛材料（以TiO 2表示）是被β-二酮螯合的氧化钛材料，并且作为主要成分的5-25％的细银颗粒材料（以Ag表示）被施加到金属表面。玻璃基板，然后用紫外线照射形成的薄膜，然后加热以制造有色薄膜涂层的玻璃制品。;版权所有：（C）2001，JPO

著录项

公开/公告号JP2001206736A

专利类型
公开/公告日2001-07-31

原文格式PDF
申请/专利权人 NIPPON SHEET GLASS CO LTD;
展开▼

申请/专利号JP20000028836
发明设计人 KAWAZU MITSUHIRO;
展开▼

申请日2000-02-07
分类号C03C17/23;
国家 JP
入库时间 2022-08-22 01:29:36