PURPOSE: To obtain a low-density, Al-Ti type heat resistant intermetallic alloy excellent in ductility and compressive strength characteristic by specifying a composition consisting of Ti, Mn, Cr, and Al. ;CONSTITUTION: This alloy is a low-density, heat resistant Al-Ti alloy excellent in ductility and compressive strength characteristic, having a composition which consists of, by atom, about 15-35% Ti, about 3-15% of Mn or Cr or Mn-Cr compound, and the balance essentially Al and further contains, if necessary, ≤about 9% V or ≤ about 9% of one element among Zr, Hf, Nb, Ta, Mo, and W and in which a part of Mn or Cr is substituted by one element among Fe, Cu, and Ni and also having a composition represented, preferably, by Al66 Mn6Ti28, Al66Cr6Ti28, Al66Mn6Ti23V5, or Al66Cr6Ti23V5. Moreover, this alloy has excellent oxidation resistance and high temp. characteristic and also has a low-density cubic structure showing superior density - (corrected strength). Further, this alloy has proper ductility at low temp. The cracking resistance of this alloy can be increased by additional V addition in particular.;COPYRIGHT: (C)1990,JPO
展开▼
机译:目的:通过指定由Ti,Mn,Cr和Al组成的成分,以获得延展性和抗压强度特性优异的低密度Al-Ti型耐热金属间合金。 ;组成:该合金是延展性和抗压强度特性极佳的低密度,耐热Al-Ti合金,其组成由原子组成,包括约15-35%的Ti,约3-15%的Mn或Cr或Mn-Cr化合物,其余部分基本为Al,并且在必要时还含有≤约9%V或≤约9%Zr,Hf,Nb,Ta,Mo和W中的一种元素Mn或Cr的一部分被Fe,Cu和Ni中的一种元素取代,并且还具有优选由Al 66 Sub> Mn 6 Sub> Ti 28 < / Sub>,Al 66 Sub> Cr 6 Sub> Ti 28 Sub>,Al 66 Sub> Mn 6 Sub> Ti 23 Sub> V 5 Sub>或Al 66 Sub> Cr 6 Sub> Ti 23 Sub> V 5 Sub>。此外,该合金具有优异的抗氧化性和高温。具有低密度的立方结构,显示出优异的密度-(校正强度)。此外,该合金在低温下具有适当的延展性。该合金的抗裂性可以通过增加V来特别提高。; COPYRIGHT:(C)1990,JPO
展开▼