A cement-based kneaded molded article having excellent bending strength and compressive strength, and a method of manufacturing the same. (Cement type kneaded molded article having high bending strength and compressive strength and method of production thereof)
A cement-based kneaded molded article having excellent bending strength and compressive strength, and a method of manufacturing the same. (Cement type kneaded molded article having high bending strength and compressive strength and method of production thereof)
A cured product of a molded product obtained by kneading a mixture of a hydraulic powder material, a potable hydraulic fine powder, a mixed water and a fine aggregate using a fine aggregate if necessary, in a specific state and curing the mixture, Or more silicate anion. The molded cured product has a compressive strength of 1000 kgf / cm 3 or more and a flexural strength of 150 kgf / cm 3 or more. Therefore, it is not necessary to use a compounding material such as special reinforcing material or fiber. Even if such a reinforcing material is used, It is possible to appropriately increase the bending strength, which is a defective characteristic of the cementitious product, in a favorable manner. In addition, it is possible to manufacture and supply a beautiful mortar or concrete product obtained by baking glaze which can not be practically practiced due to the inevitable deterioration of strength characteristics in the past, as a product secured with favorable bending strength, compressive strength and elastic modulus.
展开▼
机译：成型品的固化物，其通过将水硬性粉末材料，饮用水水硬性细粉末，混合水和细骨料的混合物根据需要使用细骨料捏合在特定状态下并使其固化而获得，或阴离子。成型的固化物的抗压强度为1000kgf / cm 3以上，抗弯强度为150kgf / cm 3以上。因此，没有必要使用诸如特殊增强材料或纤维的复合材料。即使使用这样的增强材料，也可以适当地适当地提高作为胶凝产品的不良特性的弯曲强度。此外，由于过去不可避免的强度特性的降低，因此可以制造和供应通过烘烤釉获得的美丽的砂浆或混凝土产品，该产品由于具有良好的弯曲强度，抗压强度和抗拉强度而得以确保。弹性模量。
展开▼