Flux combination of barium oxide and potassium feldspar for high- strength alumina porcelain electric insulators
Flux combination of barium oxide and potassium feldspar for high- strength alumina porcelain electric insulators
展开▼
机译:氧化钡和钾长石的助熔剂组合用于高强度氧化铝瓷电绝缘子
展开▼
页面导航
摘要
著录项
相似文献
摘要
Disclosed is an alumina porcelain composition, suitable for use after firing to form electric insulators, comprising from about 40 to 65% by weight of calcined alumina, from about 15 to 40% by weight of plastic kaolinite-montmorillonite constituents, and from about 20 to 26% by weight of a flux combination which contains alkali-aluminum silicates and from about 0.1 to 5% by weight of one or more alkaline earth oxides, preferably in the form of alkaline earth compounds. The flux combination preferably comprises about 22 to 24% by weight of potassium-aluminum silicates and from about 0.2 to 2.5% by weight of barium oxide in the form of barium compounds, thus avoiding the disadvantages associated with the use of TiO.sub.2 and MnO.sub.2.