STEEL MATERIAL SUITABLE FOR USE IN SOUR ENVIRONMENT
STEEL MATERIAL SUITABLE FOR USE IN SOUR ENVIRONMENT
展开▼
机译:适用于酸环境的钢材
展开▼
页面导航
摘要
著录项
相似文献
摘要
A steel material having a yield strength within a range of 655 to 965 MPa (95 to 125 ksi grade), and excellent SSC resistance in a low-temperature sour environment is provided. The steel material according to the present disclosure has a chemical composition consisting of, in mass%, C: 0.20 to 0.35%, Si: 0.05 to 1.00%, Mn: 0.01 to 1.00%, P: 0.025% or less, S: 0.0100% or less, Al: 0.005 to 0.100%, Cr: 0.25 to 0.80%, Mo: 0.20 to 2.00%, Ti: 0.002 to 0.050%, B: 0.0001 to 0.0050%, N: 0.0020 to 0.0100% and O: 0.0100% or less, with the balance being Fe and impurities, and satisfying Formula (1). A number density of precipitates having an equivalent circular diameter of 400 nm or more is 0.150 particles/µm2 or less. The yield strength is within a range of 655 to 965 MPa. A dislocation density ρ is 7.0×1014 m-2 or less.
展开▼
机译:提供了一种屈服强度在655至965MPa(95至125 ksi级)的屈服强度的钢材,以及在低温酸环境中的优异SSC电阻。根据本发明的钢材具有由质量%,C:0.20至0.35%,Si:0.05至1.00%,Mn:0.01至1.00%,P:0.0100的化学组合物组成%或更少,Al:0.005至0.100%,Cr:0.25至0.80%,MO:0.20至2.00%,Ti:0.002至0.050%,B:0.0001至0.0050%,N:0.0020至0.0100%和O:0.0100%或更少,平衡是Fe和杂质,并满足式(1)。等效圆径为400nm以上的沉淀物的数密度为0.150颗粒/μm 2 sup>或更少。屈服强度在655至965MPa的范围内。位错密度ρ为7.0×10 14 sup> m -2 sup>或更少。 展开▼