首页> 外国专利> Steel material suitable for use in sour environment

Steel material suitable for use in sour environment

机译：适用于酸性环境的钢材

页面导航

摘要
著录项
相似文献

摘要

The steel material according to the present disclosure contains a chemical composition consisting of, in mass %, C: 0.20 to 0.50%, Si: 0.05 to 1.00%, Mn: 0.05 to 1.00%, P: 0.025% or less, S: 0.0100% or less, Al: 0.005 to 0.100%, Cr: 0.20 to 1.50%, Mo: 0.25 to 1.50%, Ti: 0.002 to 0.050%, B: 0.0001 to 0.0050%, N: 0.0100% or less and O: 0.0100% or less, with the balance being Fe and impurities. The steel material contains an amount of dissolved C within a range of 0.010 to 0.050 mass %. The steel material also has a yield strength within a range of 965 to 1069 MPa, and a yield ratio of the steel material is 90% or more.

机译：根据本发明的钢材含有由质量％，C：0.20至0.50％，Si：0.05至1.00％，Mn：0.05至1.00％，P：0.0100的化学组合物组成％或更少，Al：0.005至0.100％，Cr：0.20至1.50％，MO：0.25至1.50％，Ti：0.002至0.050％，B：0.0001至0.0050％，N：0.0100％或更低，o：0.0100％或更少，平衡是Fe和杂质。钢材含有0.010至0.050质量％的溶解C的量。钢材的屈服强度在965至1069MPa的范围内，钢材的屈服比为90％以上。

著录项

公开/公告号US11155893B2

专利类型
公开/公告日2021-10-26

原文格式PDF
申请/专利权人 NIPPON STEEL CORPORATION;
展开▼

申请/专利号US201916977881
发明设计人 SHINJI YOSHIDA;YUJI ARAI;ATSUSHI SOMA;HIROKI KAMITANI;
展开▼

申请日2019-03-22
分类号C22C38;C21D9/46;C21D6;C21D8/02;C22C38/02;C22C38/04;C22C38/06;C22C38/20;C22C38/24;C22C38/26;C22C38/30;C22C38/44;C22C38/50;C22C38/54;
国家 US
入库时间 2022-08-24 21:53:28

相似文献

专利
外文文献
中文文献