首页> 外文会议>Fracture and strength of solids VII >Corrosion Behavior of Fe-Cr Alloys in Ar-10O_2 Atmosphere
【24h】

Corrosion Behavior of Fe-Cr Alloys in Ar-10O_2 Atmosphere

机译：Fe-Cr合金在Ar-10％O_2气氛中的腐蚀行为

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The corrosion of four Fe-Cr alloys (Cr: 9,12, 20, and 25%) with different Cr contents were subjected to cyclic oxidation fiirnace in Ar-10%O_2 atmosphere at 950℃ for 120 h. The samples after oxidation were investigated by using X-ray diffraction (XRD), optical metallography and SEM/EDS. The results indicated that increasing Cr content reduced the oxidation rate and the scale cracking. Alloys with less Cr content occurred breakaway oxidation due to formation of Fe-rich oxide scale. However, a thin protective chromia scale was observed on alloys with Cr > 20%. The corrosion behaviour on Fe-Cr alloy was then discussed based on experimental observation.
机译：对四种不同Cr含量的Fe-Cr合金（Cr：9、12、20和25％）的腐蚀在950℃的Ar-10％O_2气氛中进行了120 h的循环氧化反应。氧化后的样品通过X射线衍射（XRD），光学金相和SEM / EDS研究。结果表明，Cr含量的增加降低了氧化速率和氧化皮开裂。 Cr含量较低的合金由于形成富铁氧化物垢而发生分裂氧化。但是，在Cr> 20％的合金上观察到较薄的保护性氧化铬垢。然后根据实验观察结果讨论了铁铬合金的腐蚀行为。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号