首页> 外文会议>構造強度に関する講演会 >Compression Fatigue Failure of Impacted Carbon/Epoxy Composite Laminates

【24h】

Compression Fatigue Failure of Impacted Carbon/Epoxy Composite Laminates

机译：受冲击碳/环氧复合层压板的压缩疲劳失效

获取原文

页面导航

摘要
著录项
相似文献
相关主题

摘要

We have investigated failure mechanisms of compression fatigue behavior of impacted composite laminates. We used the two kinds of composite materials; AS4/PEEK and UT500/Epoxy, in compression fatigue test and compared the results. The endurance for impact damage of UT500/Epoxy was lower than that of AS4/PEEK. And the S-N curve of unimpacted UT500/Epoxy specimen showed a gentler gradient than that of AS4/PEEK. But their S-N curves of impacted specimens were comparatively similar.

机译：我们研究了受影响复合层压板的压缩疲劳行为的失效机制。我们使用了两种复合材料; AS4 / PEEK和UT500 /环氧树脂，在压缩疲劳试验中并比较结果。 UT500 /环氧的影响损伤的耐力低于AS4 / PEEK。并且未牵引的UT500 /环氧标本的S-N曲线显示出比AS4 / PEEK的更温和的梯度。但是受影响标本的S-N曲线相对相似。

著录项

来源
《構造強度に関する講演会》|2005年||共3页
会议地点
作者
Yasuhisa Kouno; Kazuo Kunoo; Nobuhide Uda;
展开▼
作者单位

展开▼
会议组织
原文格式 PDF
正文语种
中图分类 TD3-532;
关键词
Composites Materials; Fatigue; Fracture; Compression; Impact;

机译：复合材料;疲劳;骨折;压缩;影响;

相似文献

外文文献
中文文献
专利

1. Effects of low temperature on the mechanical properties of glass fibre-epoxy composites: static tension, compression, R=0.1 and R =-1 fatigue of +/- 45 degrees laminates [J] . Cormier Laurent, Joncas Simon, Nijssen Rogier P. L. Wind Energy . 2016,第6期

机译：低温对玻璃纤维-环氧树脂复合材料机械性能的影响：+/- 45度层压板的静态拉伸，压缩，R = 0.1和R = -1疲劳
2. Evaluation of tension-compression and tension-tension fatigue life of woven fabric glass/epoxy laminate composites used in railway vehicle [J] . Kwang-Woo Jeon, Kwang-Bok Shin, Jung-Seok Kim International Journal of Precision Engineering and Manufacturing . 2011,第5期

机译：铁路车辆用玻璃纤维/环氧层压板复合材料的拉伸压缩和拉伸疲劳寿命评估
3. Evaluation of Tension-Compression and Tension-Tension Fatigue Life of Woven Fabric Glass/Epoxy Laminate Composites used in Railway Vehicle [J] . Kwang-Woo Jeon, Kwang-Bok Shin, Jung-Seok Kim International Journal of Precision Engineering and Manufacturing . 2011,第5期

机译：铁路车辆用机织物玻璃/环氧层压复合材料的拉伸压缩和拉伸疲劳寿命评估
4. Compression Fatigue Failure of Impacted Carbon/Epoxy Composite Laminates [C] . Yasuhisa Kouno, Kazuo Kunoo, Nobuhide Uda 構造強度に関する講演会 . 2005

机译：受冲击碳/环氧复合层压板的压缩疲劳失效
5. Fatigue Life Modeling of AS4/8552 Carbon/Epoxy Composite Laminate Under Mode II Stress State [D] . Marunda, Torrence S. 2015

机译：II型应力状态下AS4 / 8552碳/环氧复合材料层压板的疲劳寿命建模
6. Compression after Impact Behaviour and Failure Analysis of Nanosilica-Toughened Thin Epoxy/GFRP Composite Laminates [O] . L. Prince Jeya Lal, S. Ramesh, S. Parasuraman, 2019

机译：纳米二氧化硅增韧的薄环氧树脂/ GFRP复合层压板的冲击行为后的压缩和失效分析
7. Experimental analysis of failures in filled hole compression tests of carbon/epoxy laminate [O] . B. Castanié, S. Crézé, J.J. Barrau, 2010

机译：碳/环氧树脂层压填充孔压缩试验中的故障试验分析
8. Comparison of Open-Hole Compression Strength and Compression After Impact Strength on Carbon Fiber/Epoxy Laminates for the Ares I Composite Interstage [R] . Hodge, A. J., Nettles, A. T., Jackson, J. R. 2011

机译：ares I复合材料级间碳纤维/环氧层压板冲击强度后的裸眼压缩强度和压缩比较

Compression Fatigue Failure of Impacted Carbon/Epoxy Composite Laminates

摘要

著录项

相似文献

相关主题

期刊订阅