Cokes play an important role of spacer in blast furnace. However, they degenerate during Boudouard reaction. Blast furnace cokes are reacted wit pure CO_2 at 1072 to 1673 K. Reaction rate was obtained by the weight change of spherical specimen. The specimen after reaction was examined by microscopic observation. The reaction rate increased with temperature and was expressed by two Arrhenius type lines. The activation energy was 126 KJ/mol at higher temperature than 1373 K and 202 KJ/mol at lower temperature range. At the higher temperature range, the reaction proceeded from the surface leaving unreacted core, whereas homogeneously whole inside at lower temperature. The porosity increased from the center to surface at higher temperature, whereas it was almost constant at lower temperature.