首页> 外文会议>International Conference on Advanced Material Engineering and Technology >Effect of Halloysite Content on Carboxymethyl Cellulose/ Halloysite Nanotube Bio-Nanocomposite Films
【24h】

Effect of Halloysite Content on Carboxymethyl Cellulose/ Halloysite Nanotube Bio-Nanocomposite Films

机译：Halloysite含量对羧甲基纤维素/霍罗伊岩纳米管生物纳米复合膜的影响

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Carboxymethyl cellulose/halloysite nanotube (CMC/HNT) bio-nanocomposite films were prepared by solution casting method. The effect of HNT content on tensile properties and morphology were studied. The results showed that the tensile strength of the CMC/HNT bio-nanocomposite films achieved optimum at 10 wt% of HNT content. The elongation at break and modulus of elasticity increased with increasing HNT content. The morphology of CMC/HNT bio-nanocomposite films showed that the poor distribution of HNT filler was observed at 20 wt% of HNT content.
机译：通过溶液浇铸方法制备羧甲基纤维素/霍氏石英纳米纤维素（CMC / HNT）生物纳米复合膜。研究了HNT含量对拉伸性能和形态的影响。结果表明，CMC / HNT生物纳米复合膜的拉伸强度在10wt％的HNT含量下最佳达到。随着HNT含量的增加，断裂和弹性模量的伸长率增加。 CMC / HNT生物纳米复合膜的形态表明，HNT填料的差分布在20wt％的HNT含量下观察到。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号