首页> 外文会议>Energy Technologies Symposium >Study of the Synthesis of MgAl_2O_4 Spinel Refractory from Waste Chromium Slag of a Chrome Plant in China
【24h】

Study of the Synthesis of MgAl_2O_4 Spinel Refractory from Waste Chromium Slag of a Chrome Plant in China

机译：中国铬厂废铬渣合成的研究

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This paper discusses the utilization of chromium slag, which presently has no useful application in China, as a resource. The following research has been done in this paper: (1) After determining the composition and properties of chromium residue we decided to test the idea of using chromium slag as a component in synthetic MgAl_2O_4 spinel material. (2) Through experiments on sintering and electric melting of refractory materials we determined the best conditions for a practical process. (3) We compared the performance of the refractory material obtained with traditional spinel refractory materials and confirmed the excellent performance of our system. The results show the feasibility of preparing MgAl_2O_4 spinel material from chromium slag by electric melting.
机译：本文讨论了铬渣的利用，目前在中国没有有用的应用，作为资源。本文进行了以下研究：（1）确定铬渣的组成和性质后，我们决定测试使用铬渣作为合成MgAl_2O_4尖晶石材料中的组分。 （2）通过对耐火材料烧结和电熔的实验，我们确定了实际过程的最佳条件。 （3）我们比较了传统尖晶石耐火材料所获得的耐火材料的性能，并确认了我们系统的优异性能。结果表明，通过电熔化从铬渣中制备MgAl_2O_4尖晶石材料的可行性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号