The Strength of Bottom Ash-Based Geopolymer Brick with Inclusion of Fly Ash.

机译：粉煤灰包装底灰基地质聚合物砖的强度。

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This paper studies the finding of compressive strength of bricks using bottom ash as a geopolymer raw material added with several percentages of fly ash, which act as a filler, besides can give better performance of strength to the bricks according to the chemical composition and the reaction of all the geopolymer materials. The study has been conducted to produce bottom ashbased geopolymer bricks by varying the percentage of fly ash added (20%, 40%, 60%, 80%) to the bottom ash-based geopolymer bricks in the mixing process. The compressive strength up to 13.69 MPa was obtained, the density is low at 20 % of fly ash added into the mixing and the water absorption is lower with the higher fly ash added using 70°C curing temperature within 24 hours at 7 days of ageing.
机译：本文研究了使用底部灰分作为底氨酸的砖块压缩强度的发现，添加了几个百分比的粉煤灰，其用作填料，除了可以根据化学成分和反应提供更好的力量对砖的力量所有地缘聚合物材料。该研究已经进行，通过改变粉煤灰（20％，40％，60％，80％）的粉煤灰在混合过程中加入底部灰分的地质聚合物砖的百分比来生产底部灰烬的地质聚合物砖。获得高达13.69MPa的抗压强度，密度低于加入混合的粉煤灰的密度低，并且吸水率较低，使用70℃固化温度在24小时后24小时后添加70℃的粉煤灰。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号