首页> 外文会议>ICTAP 2012 >Crystallite Size Characterization and Magnetism Properties of Composite (BaFe_(12)O_(19))_1-X-(SrTiO_3)X
【24h】

Crystallite Size Characterization and Magnetism Properties of Composite (BaFe_(12)O_(19))_1-X-(SrTiO_3)X

机译：复合材料的微晶尺寸表征和磁性特性（BAFE_（12）O_（19））_ 1-x-（srtio_3）x

获取原文
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A study conducted on the magnetic properties of composite material made of two materials i.e. BaFe_(12)O_(19) (Barium Hexaferrite) and SrTiO_3 (Strontium Titanate) using mechanical Alloy method. Composition proportion refers to the equation (BaFe_(12)O_(19))1-X (SrTiO_3)XX=20%, 50%,and 80% wt. Each BaFe_(12)O_(19) material produced from base material of BaCO_3 and Fe_2O_3 powder, SrTiO_3 produced from mixture of SrCO_3 and TiO_2 powder. Each material are milled for 80 hours, of which on interval 20 hours, powder is extracted for particle measurement only for X =20 % wt composition, the X= 50% wt and 80 % wt compositions are not measured. Next the material was made into bulk with 70 kN pressure die, and sintered at temperature of 1100°C for 4 hours, characterized with XRD, then magnetic character is measured with fermagraph.
机译：对由两种材料制成的复合材料磁性的一项研究，即使用机械合金法（12）o_（19）和Srtio_3（钛酸锶锶锶）。成分比例是指等式（Bafe_（12）O_（19））1-x（SRTiO_3）XX = 20％，50％和80％wt。由Baco_3和Fe_2O_3粉末的基础材料生产的每个BAFE_（12）O_（19）材料，由SRCO_3和TiO_2粉末的混合物产生的SRTIO_3。将每种材料研磨80小时，其中间隔20小时，粉末被萃取仅针对X = 20％WT组成，X = 50％wt和80％wt组合物未测量。接下来将该材料用70kN压力模具制成体积，并在1100℃的温度下烧结4小时，其特征在于XRD，然后用FermArpraph测量磁性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号