首页> 外文会议> >PHASE INTERACTIONS IN MONOCLINIC ZIRCONIA REINFORCED HYDROXYLAPATITE BIOCERAMICS
【24h】

PHASE INTERACTIONS IN MONOCLINIC ZIRCONIA REINFORCED HYDROXYLAPATITE BIOCERAMICS

机译：单相氧化锆增强羟基磷灰石生物陶瓷中的相相互作用

获取原文
获取原文并翻译 | 示例
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Hydroxylapatite composites with pure zirconia were prepared with pressureless air sintering and hot pressing for 1 hour at different temperatures between 900℃ and 1300℃. The interaction between the phases was monitored with XRD and thermal analysis. At sintering temperatures higher than 1000℃, an apparent Ca diffusion occurred from hydroxylapatite to pure zirconia phase and changed its structure from monoclinic to tetragonal/cubic. In the mean time, hydroxylapatite decomposed and formed tricalcium phosphate. Also, a reaction was occurred at 1220℃ between hydroxylapatite and zirconia phase forming CaZrO_3. The existence of air in the processing environment increased the reactivity between hydroxylapatite and zirconia.
机译：采用无压空气烧结法，在900℃至1300℃的不同温度下热压1小时，制备了纯氧化锆羟基磷灰石复合材料。用XRD和热分析监测相之间的相互作用。在高于1000℃的烧结温度下，Ca从羟基磷灰石向纯氧化锆相发生了明显的扩散，其结构从单斜晶变为四方晶/立方晶。同时，羟磷灰石分解并形成磷酸三钙。另外，在1220℃下，羟基磷灰石与氧化锆相之间发生了反应，形成CaZrO_3。加工环境中空气的存在增加了羟基磷灰石与氧化锆之间的反应性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号