Hexadecyloxylallene was prepared by the substitution reaction of propargyl alcohol with bromohexadecane and the followed rearrangement reaction. Poly(3-hexylthiophene)-b-poly( hexade-cyloxylallene) copolymers was then synthesized in one pot via sequential addition of monomers of 3-hexylthiophene and hexadecyloxylallene by using Ni(dppp)Cl2 as a single catalyst. The products were confirmed by 1H NMR and size-exclusion chromatography (SEC). The thermal, optical and electrical properties of the obtained block copolymer were investigated. The analysis of P3HT-b-PHA in the solid state using differential scanning calorimetry ( DSC ) and thermogravimetric analysis ( TGA) revealed that the material could undergo microphase separation, as two glass transition tem-peratures (Tg) and two part of the decomposition process assignable to both P3HT and PHA phases were observed. The thin-film transistors ( TFT ) with bottom-gate top-contact configuration were fabricated to characterize the electrical properties of the obtained block copolymer. The TFT devices were subsequently annealed at different temperatures (room temperature, 100, 150, and 200℃) in a glovebox under nitrogen condition. The field-effect mobility shows an increasing trend when the annealing temperature increases. Thermal annealing is performed as an effective method to optimize the device performance because it can improve the crystallinity of the thin film. Meanwhile, thermal annealing can significantly lower the effect of the residual solvent on the carrier transport, resulting in efficient charge carrier transport. When the annealing temperature is 200 ℃, polymer-based OT-FTs devices yield an average field-effect mobility of 7. 03 × 10 -4 cm2 ·V-1 ·s-1 , and a maximum field-effect mobility of 1. 3 × 10 -3 cm2 ·V-1 ·s-1 . The transfer curve shows that the threshold volt-age is 5. 44 V.%以溴代十六烷、丙炔醇为原料通过取代反应、还原重排反应制备了十六烷氧基联烯,然后以氯化(三环己基膦)镍作为催化剂,通过控制加料顺序一锅制备了聚3-己基噻吩-b-聚十六烷氧基联烯的嵌段聚合物。通过核磁共振氢谱和体积排除色谱对产物进行了表征和确证。对聚3-己基噻吩-b-聚十六烷氧基联烯嵌段聚合物的热学性能、光学性能及电学性能进行了研究。差示扫描量热法和热重分析结果表明,嵌段共聚物具有两个玻璃化转变温度及两个热分解温度,说明其具有明显相分离。以嵌段共聚物为半导体活性材料,制备了场效应晶体管器件。使用热退火对器件进行热处理,发现迁移率随退火温度的上升而提高。器件在200℃退火温度下的平均迁移率为7.03×10-4 cm2·V-1·s-1,最大迁移率为1.3×10-3 cm2·V-1·s-1,阈值电压为5.44 V。

著录项

  • 来源
    《发光学报》 |2016年第6期|669-675|共7页
  • 作者

    庞博; 葛丰; 邱龙臻;

  • 作者单位

    特种显示技术教育部重点实验室;

    特种显示技术国家工程实验室;

    现代显示技术省部共建国家重点实验室培育基地;

    合肥工业大学 光电技术研究院;

    安徽 合肥 230009;

    合肥工业大学 化学与化工学院;

    安徽 合肥 230009;

    特种显示技术教育部重点实验室;

    特种显示技术国家工程实验室;

    现代显示技术省部共建国家重点实验室培育基地;

    合肥工业大学 光电技术研究院;

    安徽 合肥 230009;

    特种显示技术教育部重点实验室;

    特种显示技术国家工程实验室;

    现代显示技术省部共建国家重点实验室培育基地;

    合肥工业大学 光电技术研究院;

    安徽 合肥 230009;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 薄膜晶体管;杂链聚合物;
  • 关键词

    有机薄膜晶体管; 聚3-己基噻吩; 一锅法; 嵌段聚合物;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号