单级固溶处理对7136铝合金组织及力学性能的影响

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effects of solution treatment on the microstructures and mechanical properties of 7136 aluminum alloy extrusion plate were studied by OM,SEM,DSC and room temperature tensile test. The results show that the higher the solution temperature and longer time, the more coarse second phase dissolved. The overheated structure appears in the alloys when the quenching temperature is at 480℃. The trend of microstructure coarsening and recrystallization appears when prolongating the solution time is extended. The suited solution of the alloy is single-stage solution of 470℃ ,4 h. After solution and peak aging of (470℃ ,4 h) + (120℃ ,24 h) ,the ultimate tensile strength,yield strength and elongation are 698 Mpa,647 Mpa and 12. 8%,respectively.%通过OM,SEM,DSC差热分析和室温拉伸性能测试,研究了单级固溶处理对7136铝合金挤压板带组织和力学性能的影响.结果表明:合金固溶处理温度越高,时间越长,粗大第二相溶解越多；合金在480℃进行固溶处理时,出现过烧组织特征.随着固溶时间的延长,呈现出晶粒粗化和再结晶组织比例增加的趋势.本合金适宜的单级固溶制度为470℃/4h,再经(120℃/24 h)峰时效处理后,合金抗拉强度、屈服强度和伸长率分别为698 MPa,47MPa和12.8％.

著录项

  • 来源
    《航空材料学报》 |2012年第5期|37-42|共6页
  • 作者

    朱冉冉; 张永安; 熊柏青; 李志辉; 李锡武; 刘红伟; 朱宝宏; 王锋;

  • 作者单位

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

    北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 轻有色金属及其合金;加热时的转变;
  • 关键词

    7136铝合金; 固溶处理; 显微组织; 力学性能;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号