首页> 中文期刊> 《机械工程材料》 >一种新型超低碳X120管线钢的显微组织

一种新型超低碳X120管线钢的显微组织

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A new kind of ultra-low carbon X120 pipeline steel was prepared in laboratory. Optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron backscattered diffraction (EBSD) were used to observe the microstructure of X120 pipeline steel. The results show that the microstructure of the steel was primarily characterized by lath-bainite and acicular ferrite. The size of the single lathbainite was 2-- 5μm in length and 0. 2 -- 0. 5 μm in width. A group of bainite laths in the size 2 -- 5 vm was composed of a number of single lath-bainite. Particles of (Nb,Ti)(C, N) and CuxS(x= 1,2) were observed, and there were high density of dislocations in bainite laths. The crystallographic orientation in a whole bainite laths was uniform, but distributed with random in different bainite laths. There were a large number of high angle boundaries and low angle boundaries among the fine bainite laths.%实验室制备了一种新型超低碳X120管线钢，采用光学显微镜、透射电镜、扫描电镜和电子背散射衍射分析技术对其显微组织进行了分析。结果表明：该管线钢的显微组织以板条贝氏体和针状铁素体为主，单个贝氏体小板条长2～5μm，宽0．2～0．5μm；若干小板条紧密结合在一起组成一组板条束，宽度为2～5μm；在板条束内部可以观察到不规则的（Nb，Ti）（C，N）和CuxS（x=1，2）颗粒，且存在高密度位错；同一板条束的晶体学取向基本一致，各板条柬之间取向无规律，板条束的各细小板条之间存在大量的大、小角度晶界。

著录项

  • 来源
    《机械工程材料》 |2012年第9期|42-46,104|共6页
  • 作者

    鲁修字; 刘静; 王贞; 贾涓; 邓照军; 彭先华; 定治明;

  • 作者单位

    武汉钢铁（集团）研究院,武汉430080 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉430081;

    武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉430081;

    武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉430081;

    武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉430081;

    武汉钢铁（集团）研究院,武汉430080;

    武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉430081;

    武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉430081;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 钢的组织与性能;
  • 关键词

    X120管线钢; 显微组织; 析出物; 贝氏体板条;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号