首页> 外文期刊>Revista Latinoamericana de Metalurgia y Materiales >EFECTO DE TRATAMIENTOS QUíMICOS Y DE PLASMA DBD EN LAS PROPIEDADES DE FIBRAS DEL SEUDOTALLO DE PLáTANO ( EFFECT OF CHEMICAL AND PLASMA DBD TREATMENTS ON PSEUDOSTEM PLANTAIN FIBER PROPERTIES )
【24h】

EFECTO DE TRATAMIENTOS QUíMICOS Y DE PLASMA DBD EN LAS PROPIEDADES DE FIBRAS DEL SEUDOTALLO DE PLáTANO ( EFFECT OF CHEMICAL AND PLASMA DBD TREATMENTS ON PSEUDOSTEM PLANTAIN FIBER PROPERTIES )

机译：化学和等离子DBD处理对假想植物纤维性能的影响对等离子DBD纤维性能的影响

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Las fibras del seudotallo de plátano (FSP) fueron modificadas mediante epiclorhidrina (EP), anhídrido acético (AA), y su combinación (AA_EP), y con plasma a tres descargas de barrera dieléctrica (DBD) 1, 3 y 6 kW min m-2. Las FSP tratadas y sin tratar fueron caracterizadas mediante espectroscopia infrarroja por la transformada de Fourier (FT-IR), termogravimetría (TGA), microscopía electrónica de barrido (SEM) y pruebas mecánicas de tensión y de humectabilidad. Los espectros FT-IR, las micrografías SEM, y el análisis TGA indicaron pérdidas de lignina, hemicelulosa, impurezas y ceras. Estos efectos en conjunto con las reacciones de grupos OH y -C-C-, con los tratamientos químicos y de plasma respectivamente, incrementaron la hidrofobicidad de las FSP tratadas. Los tratamientos químicos produjeron reacciones de esterificación, eterificación y entrecruzamiento de los grupos OH libres en las FSP, lo que hizo que mostraran mayor rigidez que las expuestas al plasma. Las micrografías SEM mostraron que las FSP expuestas al plasma quedaron con superficie más irregular y rugosa que la de las FSP tratadas químicamente. La humectabilidad de las fibras, medida mediante pruebas de ángulo de contacto, se redujo como consecuencia de ambos tratamientos, característica importante para un relleno en los materiales compuestos. Banana-plantain pseudo-stem fibers (BPF) were modified using epichlorohydrin (EP), acetic anhydride (AA), and a combination of the two (AA_EP), and three dielectric barrier discharge (DBD), plasma treatments, at 1, 3, and 6 kW min-1 m-2. Untreated and treated BPF samples were characterized via Fourier transform infrared (FT-IR) spectroscopy, thermo-gravimetric analysis (TGA), scanning electron microscopy (SEM), mechanical tensile and wettability tests. The FT-IR spectrum, the SEM images, and the TGA suggest a loss of lignin, hemicellulose, impurities, and waxes. These effects together with the modification of the OH and C-C groups, respectively by the chemical and plasma treatments, increased the hydrophobicity of the treated BPF. The chemical treatments promoted the esterification and crosslinking of the free OH groups in BPF, leading the BPF treated chemically to be more rigid than plasma-treated BPF. SEM images show that plasma-treated BPF have a rougher, more irregular surface than chemical treated BPF. The fiber wettability, measured by the contact angle assay, decreased after both treatments, which is an important characteristic for a filler material in composites.
机译：香蕉假茎（FSP）的纤维经过表氯醇（EP），乙酸酐（AA）及其组合（AA_EP）改性，并在三种介电势垒放电（DBD）为1、3和6 kW min m时具有等离子体-2。通过傅里叶变换红外光谱（FT-IR），热重分析（TGA），扫描电子显微镜（SEM）以及机械应力和润湿性测试来表征已处理和未处理的FSP。 FT-IR光谱，SEM显微照片和TGA分析表明木质素，半纤维素，杂质和蜡的损失。这些作用以及OH和-C-C-基团的反应，分别与化学和等离子体处理一起，增加了处理过的FSP的疏水性。化学处理使FSP中的游离OH基发生酯化，醚化和交联反应，这使它们显示出比暴露于等离子体中更高的刚性。 SEM显微照片显示，与化学处理的FSP相比，暴露于等离子体的FSP具有更不平坦且更粗糙的表面。两种处理均降低了通过接触角测试测得的纤维的润湿性，这是填充复合材料的重要特征。使用表氯醇（EP），乙酸酐（AA）以及两者（AA_EP）和三种介电势垒放电（DBD）的组合对香蕉-车前草假茎纤维（BPF）进行了等离子体处理，在1，3和6 kW min-1 m-2。未处理和已处理的BPF样品通过傅立叶变换红外（FT-IR）光谱，热重分析（TGA），扫描电子显微镜（SEM），机械拉伸和润湿性测试进行表征。 FT-IR光谱，SEM图像和TGA表明木质素，半纤维素，杂质和蜡的损失。这些作用以及分别通过化学和等离子体处理对OH和C-C基团的修饰，增加了处理过的BPF的疏水性。化学处理促进了BPF中游离OH基的酯化和交联，从而导致化学处理过的BPF比等离子体处理过的BPF更具刚性。 SEM图像显示，与化学处理过的BPF相比，等离子体处理过的BPF具有更粗糙，更不规则的表面。通过接触角测定法测量的纤维润湿性在两种处理之后均降低，这是复合材料中填充材料的重要特征。