首页> 外文期刊>The Open Crystallography Journal >Thick Film Laser Sintering: An Evidence for Two-step Process
【24h】

Thick Film Laser Sintering: An Evidence for Two-step Process

机译：厚膜激光烧结：两步法的证据

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The results for the sintering of Bi4Ti3O12 (BIT)-doped BaTi0.85Zr0.15O3 (BTZ) thick films, deposited by electrophoresis,using as heating source a CO2 laser are presented. The thermal process associated to the laser scanning sintering(LSS) acted in a similar way as a two-step-sintering process. This characteristic together with the high heating rate allowedus to obtain thick films with an average grain size of 200 nm, high relative density (~96%) and with a homogeneousmicrostructure. The X ray diffraction profile analysis show evidences for Bi3+ replacing Ba2+ at the A sites.
机译：给出了采用Bi2Ti3O12（BIT）掺杂的BaTi0.85Zr0.15O3（BTZ）厚膜的电泳结果，该结果是通过电泳沉积，以CO2激光器为热源进行烧结的。与激光扫描烧结（LSS）相关的热处理过程与两步烧结过程相似。此特性与高加热速率一起允许获得具有200 nm平均晶粒尺寸，高相对密度（〜96％）和均一微观结构的厚膜。 X射线衍射图谱分析显示了在A位上Bi3 +取代Ba2 +的证据。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号