首页> 外文期刊>Optical Review >Electro-Optic Coefficient Measurements for Zn x Cd1-x Te Single Crystals at 1550 nm Wavelength
【24h】

Electro-Optic Coefficient Measurements for Zn x Cd1-x Te Single Crystals at 1550 nm Wavelength

机译：Zn x Cd1-x Te单晶在1550 nm波长下的电光系数测量

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nonlinear optical materials of the type Zn x Cd1-x Te single crystals, where x = 0.0, 0.2, 0.4, 0.6, 0.7, 0.8, and 1.0, have been grown by the Bridgman method, using a vertical furnace. We have investigated the electro-optic (E-O) coefficient and refractive index of Zn x Cd1-x Te single crystals at optical communication wavelength (1550 nm). In the case of CdTe crystal, the E-O coefficient was 15.5 × 10-12 m/V, which is the biggest among the E-O coefficients of Zn x Cd1-x Te crystals. The E-O modulation signal was very big in low frequency range (DC-100kHz), but the signal amplitude became smaller as we increased frequency above 100 kHz. We also found the acousto-optic modulation at CdTe single crystals.
机译：使用Bridgman方法生长了x = 0.0、0.2、0.4、0.6、0.7、0.8和1.0的Zn x Te型单晶非线性光学材料，使用立式炉。我们研究了Zn x Te单晶在光通信波长（1550 nm）处的电光（E-O）系数和折射率。在CdTe晶体的情况下，E-O系数为15.5×10-12 m / V，在Zn x Te晶体的E-O系数中最大。在低频范围（DC-100kHz）中，E-O调制信号非常大，但是当我们将频率提高到100 kHz以上时，信号幅度会变小。我们还发现了CdTe单晶的声光调制。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号