首页> 外文期刊>Polimery >Chemically crosslinked polyethylene foams of limited flammability (Rapid Communication)
【24h】

Chemically crosslinked polyethylene foams of limited flammability (Rapid Communication)

机译：易燃性有限的化学交联聚乙烯泡沫（快速传递）

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A method to prepare chemically crosslinked polyethylene foams from a mixture consisting of polyethylene, foaming agent, crosslinking agent, antioxidant and flame retardant was discussed in this paper. The extrusion was carried out using a twin-screw extruder (temperature of barrel zones: 100, 110, 125 and 125 degrees C). Cross linking process of the extruded material was performed at 160 degrees C for 5 min. The polyethylene films were foamed in silicon oil at 225 degrees C for 2 mm. The influence of the content of flame retardant on density, hardness, flammability and tensile strength of the obtained foam was determined.
机译：本文讨论了一种由聚乙烯，发泡剂，交联剂，抗氧化剂和阻燃剂组成的混合物制备化学交联聚乙烯泡沫的方法。使用双螺杆挤出机（机筒区域的温度：100、110、125和125℃）进行挤出。挤出材料的交联过程在160摄氏度下进行5分钟。将聚乙烯膜在225℃的硅油中发泡2mm。确定了阻燃剂的含量对所得泡沫的密度，硬度，可燃性和拉伸强度的影响。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号