首页> 外文期刊>Polymers for advanced technologies >Fabrication of micropatterns with dyes in polymer films by selective doping of dye vapor in a vacuum
【24h】

Fabrication of micropatterns with dyes in polymer films by selective doping of dye vapor in a vacuum

机译：通过在真空中选择性掺杂染料蒸气，在聚合物膜中制备带有染料的微图案

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this article a novel process for patterning of dye into a positive-type novolac resin is reported by doping vapor of the blue dye, Solvent Blue 59 (SB59), using a simple vacuum process named the vapor transportation method. SB59-doped novolac resin films were examined by UV-vis absorption spectroscopy and optical microscopy. When SB59 vapor was doped into unexposed films at temperatures above 130℃, absorption peaks due to SB59 were detected. In contrast, no absorption peaks were detected when SB59 vapor was doped into exposed films. These results indicated the selective doping of SB59 vapor into unexposed novolac resin films. When SB59 vapor reached the surfaces of micropatterned novolac resin films with both unexposed and exposed areas, SB59 was doped selectively into the unexposed areas of the films, resulting in the production of micropatterns with SB59 molecules in the patterned films.
机译：在这篇文章中，报道了一种通过将蓝色染料的蒸气（称为溶剂蓝59（SB59））掺杂到蒸汽中的简单方法，将染料图案化为正型线型酚醛树脂的一种新颖方法。通过UV-可见吸收光谱法和光学显微镜检查了SB59掺杂的酚醛清漆树脂膜。当在高于130℃的温度下将SB59蒸气掺杂到未曝光的膜中时，检测到由于SB59引起的吸收峰。相反，当将SB59蒸气掺杂到曝光的膜中时，未检测到吸收峰。这些结果表明将SB59蒸气选择性地掺杂到未曝光的线型酚醛树脂膜中。当SB59蒸气到达具有未曝光和已曝光区域的微图案化线型酚醛树脂膜的表面时，将SB59选择性地掺杂到膜的未曝光区域中，从而在图案化膜中产生具有SB59分子的微图案。