首页> 外文期刊>Chemical Physics Letters >Electrochemical luminescence of ZnGa_2O_4 semiconductor electrodes activated with Cr and CO
【24h】

Electrochemical luminescence of ZnGa_2O_4 semiconductor electrodes activated with Cr and CO

机译：Cr和CO激活的ZnGa_2O_4半导体电极的电化学发光

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Electrochemical luminescence of ZnGa_2O_4:Cr and ZnGa_2O_4:Co semiconductor electrodes was studied. Under cathodic polarization in Na_2S_2O_8 electrolyte, these electrodes generated emission of ZnGa_2O_4 with a broad band from 350 to 650 nm together with red emission attributed to Cr~(3+) and Co~(2+). These emissions are explained by recombination between electrons and holes. Under anodic bias in Na_2SO_4 electrolyte, only the red emission was observed, accompanied with a sharp rise of anodic current at ca. +12.5 V.The emissions were explained by collison excitation of Cr~(3+) and Co~(2+) emission centers owing to avalanche breakdown.
机译：研究了ZnGa_2O_4：Cr和ZnGa_2O_4：Co半导体电极的电化学发光。在Na_2S_2O_8电解质中的阴极极化作用下，这些电极产生ZnGa_2O_4的发射，该发射带具有350至650 nm的宽带，并产生归因于Cr〜（3+）和Co〜（2+）的红色发射。这些发射通过电子和空穴之间的复合来解释。在Na_2SO_4电解质中的阳极偏压下，仅观察到红色发射，并伴随着约200℃的阳极电流急剧上升。 +12.5V。这种排放是由于雪崩击穿导致了Cr〜（3+）和Co〜（2+）发射中心的碰撞激发而解释的。